Spin current relaxation time in thermally evaporated naphthyl diamine derivative films

The spin relaxation time (τ) on the spin transport in thermally evaporated thin films of a naphthyl diamine derivative: N, N′-Bis(naphthalen-1-yl)-N, N′-bis(phenyl)-2,2′-dimethylbenzidine (α-NPD) was evaluated with the spin-pump-induced spin transport properties and the electrical current-voltage properties in α-NPD films. The zero-bias mobility and the diffusion constant of charges in α-NPD films were obtained to be (1.1 ± 0.4) × 10^-3 cm²/Vs and (3 ± 1) × 10^-5 cm²/s, respectively. Using these values and the previously evaluated spin diffusion length in α-NPD films of 62 ± 18 nm, the τ in α-NPD films was estimated to be 2 ± 1 μs at room temperature, under an assumption of diffusive transport of the spin current in α-NPD films. This estimated τ in α-NPD films is long enough for practical use as a spintronic molecular material.