Radial Variation of Microstructure in a Direct-Chill Cast AA7050 Billet on Homogenization
Abstract
A "through-process" solidification homogenization numerical model to study the microstructural evolution has been developed for AA7050 alloy. A continuum scale Direct Chill Casting (DCC) solidification model has been coupled with a meso-scale homogenization precipitation model to evaluate the radial variation of microstructure in a cylindrical DC cast billet after homogenization. The Local Solidification Times predicted by the DCC numerical model is used to predict the Secondary Dendritic Arm Spacing (SDAS) across the radius from an empirical relationship. It also predicts the macrosegregation used to estimate the radial as-cast microstructures (phases and phase fractions) using Thermo-Calc. Macrosegregation affects the initial and homogenized microstructures across the radius, making the surface prone to recrystallization, due to lesser dispersoids and larger precipitated particles during cooling, caused by lesser extent of Zenner pinning and Particle Stimulated Nucleation (PSN) of recrystallized grains respectively.
- Publication:
-
arXiv e-prints
- Pub Date:
- August 2023
- DOI:
- 10.48550/arXiv.2308.13800
- arXiv:
- arXiv:2308.13800
- Bibcode:
- 2023arXiv230813800P
- Keywords:
-
- Physics - Applied Physics;
- Condensed Matter - Materials Science;
- 74N25;
- G.0
- E-Print:
- 20 Pages, 8 Figures, part of the PhD Dissertation work by Pikee Priya at Purdue University (2016). Cited for reference