Evolution of complex magnetic phases and metal-insulator transition through Nb substitution in La0.5Sr0.5 Co1 −xNbx O 3
Abstract
We report the evolution of structural, magnetic, transport, and electronic properties of bulk polycrystalline La0.5Sr0.5Co1 −xNbxO3 (x = 0.025-0.25) samples. The Rietveld refinement of the x-ray diffraction patterns with R 3 ¯c space group reveals that the lattice parameters and rhombohedral distortion monotonously increase with the Nb5 +(4 d0 ) substitution (x ). The magnetic susceptibility exhibits a decrease in the magnetic ordering temperature and net magnetization with x , which manifests that the Nb substitution dilutes the ferromagnetic (FM) double-exchange interaction and enhances the antiferromagnetic (AFM) superexchange interaction. Interestingly, for the x > 0.1 samples the FM order is completely suppressed and the emergence of a glassy state is clearly evident. Moreover, the decrease in the coercivity (HC) and remanence (Mr) with x in the magnetic isotherms measured at 5 K further confirms the dominance of AFM interactions and reduction of FM volume fraction for the x > 0.1 samples. More interestingly, we observe resistivity minima for the x = 0.025 and 0.05 samples, which are analyzed using the quantum corrections in the conductivity, and found that the weak localization effect dominates over the renormalized electron-electron interactions in the three-dimensional (3D) limit. Further, a semiconducting resistivity behavior is obtained for x > 0.05, which follows the Arrhenius law at high temperatures (∼160 -320 K), and the 3D variable range hopping prevails in the low-temperature region (<160 K). The core-level photoemission spectra confirm the valence state of constituent elements and the absence of Co2 + is discernible.
- Publication:
-
Physical Review B
- Pub Date:
- April 2023
- DOI:
- 10.1103/PhysRevB.107.165108
- arXiv:
- arXiv:2303.01108
- Bibcode:
- 2023PhRvB.107p5108S
- Keywords:
-
- Condensed Matter - Strongly Correlated Electrons;
- Condensed Matter - Materials Science
- E-Print:
- submitted