Uniaxial ferromagnetism in the kagome metal TbV6Sn6
Abstract
The synthesis and characterization of the vanadium-based kagome metal Tb V 6Sn 6 is presented. X-ray measurements confirm that this material forms with the same crystal structure type as the recently investigated kagome metals Gd V6Sn6 and Y V6Sn6 , with space group symmetry P 6 /m m m . A signature of a phase transition at 4.1 K is observed in heat capacity, resistivity, and magnetic susceptibility measurements, and both resistivity and magnetization measurements exhibit hysteresis in magnetic field. Furthermore, a strikingly large anisotropy in the magnetic susceptibility was observed, with the c -axis susceptibility roughly 75 times the a b plane susceptibility at 5 K. This is highly suggestive of uniaxial ferromagnetism, and the large size of 9.4 μb/f .u . indicates the Tb3 +4 f electronic moments cooperatively align perpendicular to the V kagome lattice plane. The entropy at the phase transition is nearly R ln(2), indicating that the crystalline electric field ground state of the Tb3 + ion is a doublet, and therefore the sublattice of 4 f electrons in this material can be shown to map at low temperatures to the Ising model in a D6 h symmetry environment. Hall measurements at temperatures from 300 to 1.7 K can be described by two-band carrier transport at temperatures below around 150 K, with a large increase in both hole and electron mobilities, similar to Y V6Sn6 , and an anomalous Hall effect is seen below the ordering temperature. Angle-resolved photoemission measurements above the magnetic ordering temperature reveal typical kagome dispersions. Our study presents Tb V 6Sn 6 as an interesting system where Ising ferromagnetism coexists with nontrivial electronic states emerging from a kagome lattice.
- Publication:
-
Physical Review B
- Pub Date:
- September 2022
- DOI:
- 10.1103/PhysRevB.106.115139
- arXiv:
- arXiv:2205.14802
- Bibcode:
- 2022PhRvB.106k5139R
- Keywords:
-
- Condensed Matter - Strongly Correlated Electrons
- E-Print:
- doi:10.1103/PhysRevB.106.115139