Robust antiferromagnetism in Y2Co3
Abstract
We report on a solution-growth based method to synthesise single crystals of Y2Co3 and on its structural and magnetic properties. We find that Y2Co3 crystallizes in the La2Ni3 -type orthorhombic structure with space group C m c e (No. 64), with Co forming distorted kagome lattices. Y2Co3 orders antiferromagnetically below TN=252 K. Magnetization measurements reveal that the moments are primarily aligned along the b axis with evidence for some canting. Band-structure calculations indicate that ferromagnetic and antiferromagnetic orders are nearly degenerate, at odds with experimental results. Magnetization measurements under pressure up to 1 GPa reveal that the Néel temperature decreases with the slope of −1.69 K/GPa. We observe a field-induced spin-flop transition in the magnetization measurements at 1.5 K and 21 T with magnetic field along the b direction. The magnetization is not saturated up to 35 T, indicating that the antiferromagnetic ordering in Y2Co3 is quite robust, which is surprising for such a Co-rich intermetallic.
- Publication:
-
Physical Review B
- Pub Date:
- November 2021
- DOI:
- 10.1103/PhysRevB.104.184407
- arXiv:
- arXiv:2201.11778
- Bibcode:
- 2021PhRvB.104r4407S
- Keywords:
-
- Condensed Matter - Strongly Correlated Electrons;
- Condensed Matter - Materials Science
- E-Print:
- Physical Review B 104, 184407 (2021)