Tetragonality mapping of martensite in a high-carbon steel by EBSD
Abstract
The locally varying tetragonality in martensite grains of a high-carbon steel (1.2 mass percent C) was resolved by electron backscatter diffraction (EBSD) with a spatial resolution in the order of 100nm. Compared to spatially integrating X-ray diffraction, which yielded an average tetragonality of c/a=1.05, the EBSD measurements in the scanning electron microscope allowed to image a local variation of the lattice parameter ratio c/a in the range of 1.02 $\leq$ c/a $\leq$ 1.07. The local variation of tetragonality is confirmed by two different EBSD data analysis approaches based on the fitting of simulated to experimental EBSD patterns. The resulting EBSD-based tetragonality maps are pointing to a complex interaction of carbon concentration and local lattice distortions during the formation process of martensitic structures.
- Publication:
-
arXiv e-prints
- Pub Date:
- November 2020
- DOI:
- 10.48550/arXiv.2011.10275
- arXiv:
- arXiv:2011.10275
- Bibcode:
- 2020arXiv201110275N
- Keywords:
-
- Condensed Matter - Materials Science
- E-Print:
- 16 pages, 9 figures