Wafer-scale fabrication of two-dimensional beta-In2Se3 photodetectors
Abstract
The epitaxial growth of two-dimensional (2D) $\beta-In_2Se_3$ material was obtained over 2-inches c-sapphire wafers using molecular beam epitaxy (MBE). Excellent quality of thick (90 nm) and very thin films, down to two quintuple layers (2 nm), was confirmed by x-ray diffraction (XRD), Raman spectroscopy, and aberration-corrected scanning transmission electron microscopy (ac-STEM). Wafer-scale fabrication of photodetectors based on five quintuple layers was produced using photolithography and other standard semiconductor processing methods. The photodetectors exhibit responsivity of 3 mA/W, peak specific detectivity (D*) of $10^9$ Jones, external quantum efficiency (EQE) of 0.67 % at 550 nm, and response-time of ~7 ms, which is faster than any result previously reported for $\beta-In_2Se_3$ photodetectors. From the photocurrent measurements, an optical bandgap of 1.38 eV was observed. These results on wafer-scale deposition of 2D $In_2Se_3$, as well as its fabrication into optoelectronic devices provide the missing link that will enable the commercialization of 2D materials.
- Publication:
-
arXiv e-prints
- Pub Date:
- May 2020
- DOI:
- 10.48550/arXiv.2005.10819
- arXiv:
- arXiv:2005.10819
- Bibcode:
- 2020arXiv200510819C
- Keywords:
-
- Condensed Matter - Materials Science;
- Condensed Matter - Mesoscale and Nanoscale Physics;
- Physics - Applied Physics
- E-Print:
- Advanced Optical Materials, 2020, 2001034