Polar state of 0.67BiFeO3-0.33BaTiO3 near the morphotropic phase boundary
Abstract
The symmetric studies on the structure-property relationship of the unpoled and poled states of 0.67BiFeO3-0.33BaTiO3 (0.67BF-0.33BT) were conducted to understand the origin of the morphotropic phase boundary (MPB) in BF-BT. A typical relaxor-type dielectric anomaly was observed (Tf, ~627 K). The remnant polarization (Pr) and maximum value of electro-strain (Sm) increase clearly during heating (Pr, ~40 uC/cm2; Sm, 0.191 % under 40 kV/cm at 453 K). The first-cycle electro-strain loops indicate the difference in the polar state between 0.67BF-0.33BT and 0.94BiNaTiO3-0.06BaTiO3. Both the unpoled and poled samples have the similar frequency dispersion behaviors. Even in the poled samples, the transition between the ergodic relaxor state and ferroelectric-like state does not involve a clear dielectric anomaly. Analyses based on the Rietveld refinement of XRD patterns, bright-field images and selected-area electron diffractions (SAED) demonstrated that the formation of the long-range ferroelectric domains was difficult under the poling field.
- Publication:
-
arXiv e-prints
- Pub Date:
- February 2020
- DOI:
- 10.48550/arXiv.2002.05312
- arXiv:
- arXiv:2002.05312
- Bibcode:
- 2020arXiv200205312W
- Keywords:
-
- Condensed Matter - Materials Science