Electrochemical analysis of Na0.7Co1-xNbxO2(x = 0, 0.05) as cathode materials in sodium-ion batteries

Sodium-ion batteries (SIBs) have received significant attention as promising alternative for energy storage applications owing to the large availability and low cost of sodium. In this paper we study the electrochemical behavior of Na_0.7Co_1-xNbxO₂ (x = 0 and 0.05 samples), synthesized via solid-state reaction. The Rietveld refinement of x-ray diffraction pattern reveals the hexagonal crystal symmetry with P63/mmc space group. The Na_0.7Co_0.95Nb_0.05O₂ cathode exhibits a specific capacity of about 91 mAhg^-1 at a current density of 6mAg^-1, whereas Na_0.7CoO₂ exhibits comparatively low specific capacity (70 mAhg^-1 at a current density of 6mAg^-1). The cyclic voltammetry (CV) and electron impedance spectroscopy (EIS) were performed to determine the diffusion coefficient of Na, which found to be in the range of 10^-9 - 10^-10 cm²s^-1.