Disorder-induced ferrimagnetism in sputtered Mn$_{x}$CoGe thin films
Abstract
Investigations into the magnetic properties of sputtered Mn$_{x}$CoGe films in the range $0.8 \leq x \leq 2.5$ uncovered ferrimagnetic order, unlike the ferromagnetic order reported in bulk samples. These films formed hexagonal Ni$_{2}$In-type structures when annealed at temperatures below 600$^{\circ}$C. While the Curie temperatures of the films are comparable to those of hexagonal bulk MnCoGe, there is a reduction in the magnetization of the Mn$_{x}$CoGe films relative to bulk MnCoGe, and a magnetization compensation point is observed in the $x<1$ samples. To understand the behavior, we calculated the magnetic moments of Mn-antisite defects in MnCoGe with density-function theory (DFT) calculations. Models constructed from the calculation suggest that films become ferrimagnetic due to the presence of Mn on the Co and Ge sites. In the $x<1$ samples, these defects arose from the disorder in the films, whereas for $x>1$, the excess Mn was driven onto the antisites. Mean field modeling of the temperature dependence of the magnetization provides additional evidence for ferrimagnetism. Our mean field and DFT models provide a description of how the variation in film defects with composition will transition the magnetic behavior from a compensated (V-type) to an uncompensated (Q-type) ferrimagnet.
- Publication:
-
arXiv e-prints
- Pub Date:
- September 2019
- DOI:
- 10.48550/arXiv.1910.00124
- arXiv:
- arXiv:1910.00124
- Bibcode:
- 2019arXiv191000124K
- Keywords:
-
- Condensed Matter - Materials Science;
- Physics - Applied Physics
- E-Print:
- 11 pages, 10 figures