Superconductivity of Electron-Doped NdOBiS2 by Substitution of Mixed-Valence Ce Ions

Superconductivity is achieved in Nd_1-xCe_xOBiS₂ via electron doping using mixed-valence Ce ions. Single crystals with x = 0.2, 0.3, 0.4, and 0.5 are generated using a CsCl flux method. Plate-like single crystals with dimensions of 0.8 × 0.8 × 0.2 mm³ were obtained. The magnetic susceptibility χ(T) indicates large diamagnetism, and the electrical resistivity ρ(T) indicates zero resistivity. The maximum value of T_c is observed at 4.7 K in Nd_0.8Ce_0.2OBiS₂ from χ(T). From the ρ(T) measurements taken in several magnetic fields, the upper critical field μ₀H_c2(0) is estimated to be ∼12 and ∼0.34 T for the ab- and c-planes, respectively. We redetermined μ₀H_c2(0) of NdO_0.7F_0.3BiS₂, as ∼35 and ∼0.78 T for the ab- and c-planes, respectively. The anisotropic parameter Γ is estimated to be ∼35 for Nd_0.7Ce_0.3OBiS₂ and ∼45 for NdO_0.7F_0.3BiS₂. The μ₀H_c2(0) of Nd_0.7Ce_0.3OBiS₂ is approximately two times smaller than that of NdO_0.7F_0.3BiS₂, although the difference of Γ is approximately 10.