On the Characterization of a Hitherto Unreported Icosahedral Quasicrystal Phase in Additively Manufactured Aluminum Alloy AA7075
Abstract
Aluminum alloy AA7075 (Al-Zn-Mg-Cu) specimens were prepared using selective laser melting, also known as powder bed fusion additive manufacturing. In the as-manufactured state, which represents a locally rapidly solidified condition, the prevalence of a previously unreported icosahedral quasicrystal with 5-fold symmetry was observed. The icosahedral quasicrystal, which has been termed ν-phase (nu-phase), was comprised of Zn, Cu, and Mg.
- Publication:
-
Metallurgical and Materials Transactions A
- Pub Date:
- February 2019
- DOI:
- 10.1007/s11661-018-5025-1