High-pressure polymorphism of BaFe2Se3
Abstract
BaFe2Se3 is a potential superconductor material exhibiting transition at 11 K and ambient pressure. Here we extended the structural and performed electrical resistivity measurements on this compound up to 51 GPa and 20 GPa, respectively, in order to distinguish if the superconductivity in this sample is intrinsic to the BaFe2Se3 phase or if it is originating from minor FeSe impurities that show a similar superconductive transition temperature. The electrical resistance measurements as a function of pressure show that at 5 GPa the superconducting transition is observed at around 10 K, similar to the one previously observed for this sample at ambient pressure. This indicates that the superconductivity in this sample is most likely intrinsic to the BaFe2Se3 phase and not to FeSe with Tc > 20 K at these pressures. Further increase in pressure suppressed the superconductive signal and the sample remained in an insulating state up to the maximum achieved pressure of 20 GPa.
- Publication:
-
Journal of Physics Condensed Matter
- Pub Date:
- February 2019
- DOI:
- 10.1088/1361-648X/aaf777
- arXiv:
- arXiv:1808.03952
- Bibcode:
- 2019JPCM...31h5401S
- Keywords:
-
- superconductivity;
- structure;
- high pressure;
- Condensed Matter - Superconductivity
- E-Print:
- J. Phys.: Condens. Matter 31 (2019) 085401