Coherently strained epitaxial YBa2Cu3O7-δ films grown on NdGaO3 (110)

YBa₂Cu₃O_7-δ is a good candidate to systematically study high-temperature superconductivity by nanoengineering using advanced epitaxy. An essential prerequisite for these studies is coherently strained YBa₂Cu₃O_7-δ thin films, which we present here using NdGaO₃ (110) as a substrate. The films are coherent up to at least 100 nm thickness and have a critical temperature of 89 ± 1 K. The a and b lattice parameters of YBa₂Cu₃O_7-δ are matched to the in-plane lattice parameters of NdGaO₃ (110), resulting in a large reduction of the orthorhombicity of YBa₂Cu₃O_7-δ. These results imply that a large amount of structural disorder in the chain layers of YBa₂Cu₃O_7-δ is not detrimental to superconductivity.