Crystal growth, characterization, and point-contact Andreev-reflection spectroscopy of the noncentrosymmetric superconductor Mo3Al2C
Abstract
We report on the first successful growth of single crystals of the noncentrosymmetric superconductor Mo3Al2C obtained by means of a cubic-anvil, high-pressure, and high-temperature technique. Composition, structure, and normal-state transport properties of the crystals were studied by means of x-ray diffraction, energy-dispersive x-ray spectroscopy, magnetic susceptibility, and resistivity measurements as a function of temperature. Variations in critical temperature (Tc) between 8.6 and 9.3 K were observed, probably due to the slightly different carbon stoichiometry of the samples. Single-crystal x-ray refinement confirmed the high structural perfection of the grown crystals. Remarkably, the refined Flack parameter values for all the measured crystals using a P 4132 space-group model were consistently close to either 0 or 1, hence indicating that the considered crystals belong to two enantiomorphic space groups, P 4132 and P 4332 . An anomaly in the resistivity is observed at ≃130 K, most likely associated with the onset of a charge-density-wave phase. The superconducting properties (and in particular the symmetry, the amplitude, and the temperature dependence of the superconducting gap) were studied by using point contact Andreev-reflection spectroscopy. The results confirm that Mo3Al2C is a moderately strongly-coupled superconductor with 2 Δ /kBTc≃4 and unambiguously prove that the order parameter has an s -wave symmetry despite the asymmetric spin-orbit coupling arising from the lack of inversion symmetry.
- Publication:
-
Physical Review B
- Pub Date:
- June 2018
- DOI:
- 10.1103/PhysRevB.97.214518
- arXiv:
- arXiv:1803.08366
- Bibcode:
- 2018PhRvB..97u4518Z
- Keywords:
-
- Condensed Matter - Superconductivity
- E-Print:
- 12 pages, 12 figures, revtex format