Glass Transitions, Semiconductor-Metal Transitions, and Fragilities in Ge -V -Te (V =As , Sb) Liquid Alloys: The Difference One Element Can Make
Abstract
Glass-transition temperatures (Tg ) and liquid fragilities are measured along a line of constant Ge content in the system Ge-As-Te, and contrasted with the lack of glass-forming ability in the twin system Ge-Sb-Te at the same Ge content. The one composition established as free of crystal contamination in the latter system shows a behavior opposite to that of a more covalent system. The comparison of Tg vs bond density in the three systems Ge-As-chalcogen differing in chalcogen, i.e., S, Se, or Te, shows that as the chalcogen becomes more metallic, i.e., in the order S <Se <Te , the bond-density effect on Tg becomes systematically weaker, with a crossover at ⟨r ⟩=2.3 . When the more metallic Sb replaces As at ⟨r ⟩ greater than 2.3, incipient metallicity rather than directional bond covalency apparently gains control of the physics. This observation leads us to an examination of the electronic conductivity and then semiconductor-to-metal (SC-M ) transitions, with their associated thermodynamic manifestations in relevant liquid alloys. The thermodynamic components, as seen previously, control liquid fragility and cause fragile-to-strong transitions during cooling. We tentatively conclude that liquid-state behavior in phase-change materials is controlled by liquid-liquid (LL) and SC-M transitions that have become submerged below the liquidus surface. In the case of the Ge-Te binary, a crude extrapolation to GeTe stoichiometry indicates that the SC-M transition lies about 20% below the melting point, suggesting a parallel with the intensely researched "hidden liquid-liquid transition" in supercooled water. In the water case, superfast crystallization initiates in the high-fragility domain some 4% above the LL transition temperature (TLL ) which is located at approximately 15% below the (ambient pressure) melting point.
- Publication:
-
Physical Review Applied
- Pub Date:
- March 2017
- DOI:
- 10.1103/PhysRevApplied.7.034035
- arXiv:
- arXiv:1610.08164
- Bibcode:
- 2017PhRvP...7c4035W
- Keywords:
-
- Condensed Matter - Materials Science
- E-Print:
- Phys. Rev. Applied 7, 034035 (2017)