Structural and magnetic characterization of the one-dimensional S = 5 /2 antiferromagnetic chain system SrMn (V O4) (OH )

The descloizite-type compound, SrMn (V O₄) (OH ) , was synthesized as large single crystals (1-2 mm) using a high-temperature high-pressure hydrothermal technique. X-ray single crystal structure analysis reveals that the material crystallizes in the acentric orthorhombic space group of P 2₁2₁2₁ (no. 19), Z = 4 . The structure exhibits a one-dimensional feature, with [Mn_O4]∞ chains propagating along the a axis, which are interconnected by V O₄ tetrahedra. Raman and infrared spectra were obtained to identify the fundamental vanadate and hydroxide vibrational modes. Magnetization data reveal a broad maximum at approximately 80 K, arising from one-dimensional magnetic correlations with intrachain exchange constant of J /k_B= 9.97 (3 ) K between nearest Mn neighbors and a canted antiferromagnetic behavior below T_N= 30 K . Single crystal neutron diffraction at 4 K yielded a magnetic structure solution in the lower symmetry of the magnetic space group P 2₁ with two unique chains displaying antiferromagnetically ordered Mn moments oriented nearly perpendicular to the chain axis. The presence of the Dzyaloshinskii-Moriya antisymmetric exchange interaction leads to a slight canting of the spins and gives rise to a weak ferromagnetic component along the chain direction.