Novel Cross-Slip Mechanism of Pyramidal Screw Dislocations in Magnesium
Abstract
Compared to cubic metals, whose primary slip mode includes twelve equivalent systems, the lower crystalline symmetry of hexagonal close-packed metals results in a reduced number of equivalent primary slips and anisotropy in plasticity, leading to brittleness at the ambient temperature. At higher temperatures, the ductility of hexagonal close-packed metals improves owing to the activation of secondary ⟨c +a ⟩ pyramidal slip systems. Thus, understanding the fundamental properties of corresponding dislocations is essential for the improvement of ductility at the ambient temperature. Here, we present the results of large-scale ab initio calculations for ⟨c +a ⟩ pyramidal screw dislocations in magnesium and show that their slip behavior is a stark counterexample to the conventional wisdom that a slip plane is determined by the stacking fault plane of dislocations. A stacking fault between dissociated partial dislocations can assume a nonplanar shape with a negligible energy cost and can migrate normal to its plane by a local shuffling of atoms. Partial dislocations dissociated on a {2 1 ¯ 1 ¯ 2 } plane "slither" in the {01 1 ¯1 } plane, dragging the stacking fault with them in response to an applied shear stress. This finding resolves the apparent discrepancy that both {2 1 ¯1 ¯2 } and {01 1 ¯1 } slip traces are observed in experiments while ab initio calculations indicate that dislocations preferably dissociate in the {2 1 ¯1 ¯2 } planes.
- Publication:
-
Physical Review Letters
- Pub Date:
- June 2016
- DOI:
- 10.1103/PhysRevLett.116.225501
- arXiv:
- arXiv:1605.02946
- Bibcode:
- 2016PhRvL.116v5501I
- Keywords:
-
- Condensed Matter - Materials Science
- E-Print:
- RevTex, 12 pages, 6 figures, Accepted for publication in Phys.Rev.Lett. (v2: figure resolution improved)