Saturation of ion irradiation effects in MAX phase Cr2AlC
Abstract
Cr2AlC materials were irradiated with 7 MeV Xe26+ ions and 500 keV He2+ ions at room temperature. A structural transition with an increased c lattice parameter and a decreased a lattice parameter occurs after irradiation to doses above 1 dpa. Nevertheless, the modified structure is stable up to the dose of 5.2 dpa without obvious lattice disorder. The three samples irradiated to doses above 1 dpa have comparable lattice parameters, hardness and modulus values, suggesting a saturation of irradiation effects in Cr2AlC. The structural transition and irradiation effects saturation are ascribed to irradiation-induced antisite defects (CrAl and AlCr) and C interstitials, which is supported by the calculations of the formation energies of various defects in Cr2AlC. The irradiation-induced antisite defects and C interstitials may be critical to understand the excellent resistance to irradiation-induced amorphization of MAX phases.
- Publication:
-
Acta Materialia
- Pub Date:
- May 2016
- DOI:
- 10.1016/j.actamat.2016.03.021
- arXiv:
- arXiv:1601.05514
- Bibcode:
- 2016AcMat.110....1H
- Keywords:
-
- MAX phases;
- Ion irradiation;
- Rietveld refinement;
- Defect formation energy;
- Condensed Matter - Materials Science
- E-Print:
- 14 pages, 8 figures