Measurement of the penetration depth and coherence length of MgB 2 in all directions using transmission electron microscopy

We demonstrate that images of flux vortices in a superconductor taken with a transmission electron microscope can be used to measure the penetration depth and coherence length in all directions at the same temperature and magnetic field. This is particularly useful for MgB ₂, where these quantities vary with the applied magnetic field and values are difficult to obtain at low field or in the c direction. We obtained images of flux vortices from a MgB ₂ single crystal cut in the a c plane by focused ion beam milling and tilted to 45^∘ with respect to the electron beam about the crystallographic a axis. A new method was developed to simulate these images that accounted for vortices with a nonzero core in a thin, anisotropic superconductor and a simplex algorithm was used to make a quantitative comparison between the images and simulations to measure the penetration depths and coherence lengths. This gave penetration depths Λ_{a b}=100 ±35 nm and Λ_c=120 ±15 nm at 10.8 K in a field of 4.8 mT. The large error in Λ_{a b} is a consequence of tilting the sample about a and had it been tilted about c , the errors on Λ_{a b} and Λ_c would be reversed. Thus obtaining the most precise values requires taking images of the flux lattice with the sample tilted in more than one direction. In a previous paper [J. C. Loudon et al., Phys. Rev. B 87, 144515 (2013), 10.1103/PhysRevB.87.144515], we obtained a more precise value for Λ_{a b} using a sample cut in the a b plane. Using this value gives Λ_{a b}=107 ±8 nm, Λ_c=120 ±15 nm, ξ_{a b}=39 ±11 nm, and ξ_c=35 ±10 nm, which agree well with measurements made using other techniques. The experiment required two days to conduct and does not require large-scale facilities. It was performed on a very small sample, 30 ×15 μ m and 200-nm thick, so this method could prove useful for superconductors where only small single crystals are available, as is the case for some iron-based superconductors.