Single phase synthesis and room temperature neutron diffraction studies on multiferroic PbFe0.5Nb0.5O3
Abstract
The lead-iron-niobate, (PbFe0.5Nb0.5O3 or PFN) was synthesized by low temperature sintering Single Step / Solid State Reaction Method. The 700 °C/2 hrs. calcined powder was sintered at 1050 °C/1 hr. The sintered pellets were characterized through X-Ray Diffraction and Neutron Diffraction at room temperature. It is found from the XRD pattern that the materials is in single phase with no traces of pyrochlore phase. It was also confirmed from the neutron diffraction pattern, the structure of PFN to be monoclinic, space group Cm. Structural studies has been carried out by refining the obtained neutron diffraction data by Rietveld refinement method using Fullprof program. The neutron diffraction pattern at 300 K (room temperature) was selected to refine the structure. The lattice parameters obtained are; a = 5.6709 Å, b = 5.6732 Å, c = 4.0136 Å, and α = 90, β = 89.881, γ = 90. The P-E measurements showed hysteretic behavior with high remnant polarization.
- Publication:
-
Solid State Physics
- Pub Date:
- February 2013
- DOI:
- 10.1063/1.4791496
- arXiv:
- arXiv:1501.00553
- Bibcode:
- 2013AIPC.1512.1232M
- Keywords:
-
- calcination;
- dielectric hysteresis;
- dielectric polarisation;
- ferroelectric ceramics;
- iron compounds;
- lattice constants;
- lead compounds;
- multiferroics;
- neutron diffraction;
- powder technology;
- sintering;
- space groups;
- X-ray diffraction;
- 61.66.Fn;
- 75.85.+t;
- 77.22.Ej;
- 77.80.Dj;
- 77.84.Ek;
- 81.05.Je;
- Inorganic compounds;
- Polarization and depolarization;
- Domain structure;
- hysteresis;
- Ceramics and refractories;
- Condensed Matter - Materials Science
- E-Print:
- 2 pages, 3 Figures