Effects of post-annealing and cobalt co-doping on superconducting properties of (Ca,Pr)Fe2As2 single crystals

In order to clarify the origin of anomalous superconductivity in (Ca,RE)Fe₂As₂ system, Pr doped and Pr,Co co-doped CaFe₂As₂ single crystals were grown by the FeAs flux method. These samples showed two-step superconducting transition with T_c1 = 25-42 K, and T_c2 < 16 K, suggesting that (Ca,RE)Fe₂As₂ system has two superconducting components. Post-annealing performed for these crystals in evacuated quartz ampoules at various temperatures revealed that post-annealing at ∼400 °C increased the c-axis length for all samples. This indicates that as-grown crystals have a certain level of strain, which is released by post-annealing at ∼400 °C. Superconducting properties also changed dramatically by post-annealing. After annealing at 400 °C, some of the co-doped samples showed large superconducting volume fraction corresponding to the perfect diamagnetism below T_c2 and high J_c values of 10⁴-10⁵ A cm^-2 at 2 K in low field, indicating the bulk superconductivity of (Ca,RE)Fe₂As₂ phase occurred below T_c2. On the contrary, the superconducting volume fraction above T_c2 was always very small, suggesting that 40 K-class superconductivity observed in this system is originating in the local superconductivity in the crystal.