Crystallography and physical properties of BaCo2As2,Ba0.94K0.06Co2As2, and Ba0.78K0.22Co2As2

The crystallographic and physical properties of polycrystalline and single-crystal samples of BaCo₂As₂ and K-doped Ba_1-xK_xCo₂As₂ (x=0.06,0.22) are investigated by x-ray and neutron powder diffraction, magnetic susceptibility χ, magnetization, heat capacity C_p,As_{75 nuclear magnetic resonance (NMR), and electrical resistivity ρ measurements versus temperature T. The crystals were grown using both Sn flux and CoAs self-flux, where the Sn-grown crystals contain 1.6-2.0 mol% Sn. All samples crystallize in the tetragonal ThCr2}Si₂-type structure (space group I4/m_{mm). For BaCo2As2, powder neutron diffraction data show that the c-axis lattice parameter exhibits anomalous negative thermal expansion from 10 K to 300 K, whereas the a axis lattice parameter and the unit cell volume show normal positive thermal expansion over this T range. No transitions in BaCo2As2 were found in this T range from any of the measurements. Below 40-50 K, we find ρ ∝T², indicating a Fermi liquid ground state. A large density of states at the Fermi energy D (EF)≈18 states/(eV f.u.) for both spin directions is found from low-T Cp(T) measurements, whereas the band-structure calculations give D (EF)=8.23 states/(eV f.u.). The enhancement of the former value above the latter is inferred to arise from electron-electron correlations and the electron-phonon interaction. The derived intrinsic χ (T) monotonically increases with decreasing T, with anisotropy χab>χc. The ⁷⁵As-NMR shift data versus T have the same T dependence as the derived χ (T) data, demonstrating that the derived χ (T) data are intrinsic. The observed ⁷⁵As nuclear spin dynamics rule out the presence of Néel-type antiferromagnetic electronic spin fluctuations, but are consistent with the presence of ferromagnetic and/or stripe-type antiferromagnetic spin fluctuations. The crystals of Ba0.78}K_0.22Co₂As₂ were grown in Sn flux and show properties very similar to those of undoped BaCo₂As₂. On the other hand, the crystals from two batches of Ba_0.94K_0.06Co₂As₂ grown in CoAs self-flux show evidence of weak ferromagnetism at T ≲10 K with small ordered moments at 1.8 K of ≈0.007 and 0.03μ_B per formula unit, respectively.