Single crystal study of the layered heavy fermion compounds Ce2PdIn8, Ce3PdIn11, Ce2PtIn8 and Ce3PtIn11

We report on single crystal growth and crystallographic parameters results of Ce₂PdIn₈, Ce₃PdIn_11, Ce₂PtIn₈ and Ce₃PtIn₁₁. The Pt-systems Ce₂PtIn₈ and Ce₃PtIn₁₁ are synthesized for the first time. All these compounds are member of Ce_nT_mIn_3n+2m (n=1, 2,..; m=1, 2,.. and T= transition metal) to which the extensively studied heavy fermion superconductor CeCoIn₅ belongs. Single crystals have been grown by an In self-flux method. Differential scanning calorimetry studies were used to derive optimal growth conditions. Evidently, the maximum growth conditions for these materials should not exceed 750 °C. Single crystal x-ray data show that Ce₂TIn₈ compounds crystallize in the tetragonal Ho₂CoGa₈ phase (space group P4/mmm) with lattice parameters a=4.6898(3) Å and c=12.1490(8) Å for Pt-based one (Pd: a=4.6881(4) Å and c=12.2031(8) Å). Ce₃TIn₁₁ compounds adopt Ce₃PdIn₁₁ structure with a=4.6874(4) Å and c=16.8422(12) Å for Pt-based one (Pd: a=4.6896 Å and c=16.891 Å). Specific heat experiments on Ce₃PtIn₁₁ and Ce₃PdIn₁₁ have revealed that both compounds undergo two successive magnetic transitions at T₁ ~2.2 K followed by T_N ~2.0 K and T₁ ~1.7 K and T_N ~1.5 K, respectively. In addition, both compounds exhibit enhanced Sommerfeld coefficients yielding γ_Pt=0.300 J/mol K² Ce (γ_Pd=0.29 J/mol K² Ce), hence qualifying them as heavy fermion materials.