Effect of growth oxygen pressure on anisotropic-strain-induced phase separation in epitaxial La0.67Ca0.33MnO3/NdGaO3(001) films
Abstract
The effect of deposition oxygen pressure (PO) on phase separation (PS) induced in epitaxial La0.67Ca0.33MnO3/NdGaO3(001) films was investigated. Fully oxygenated films grown at high PO are anisotropically strained. They exhibit PS over a wide temperature range, because of the large orthorhombicity of NdGaO3 substrates. The paramagnetic insulator-to-ferromagnetic metal (FM) and FM-to-antiferromagnetic insulator (AFI) transitions gradually shift to lower temperatures with decreasing PO. The AFI state is initially weakened (PO ≥ 30 Pa), but then becomes more robust against the magnetic field (PO < 30 Pa). The out-of-plane film lattice parameter increases with decreasing PO. For films grown at PO ≥ 30 Pa, the slight oxygen deficiency may enlarge the lattice unit cell, reduce the anisotropic strain, and suppress the AFI state. Films deposited at PO < 30 Pa instead experience an average compressive strain. The enhanced compressive strain and structural defects in the films may lead to the robust AFI state. These results aid our understanding of PS in manganite films.
- Publication:
-
Journal of Applied Physics
- Pub Date:
- May 2013
- DOI:
- 10.1063/1.4807293
- arXiv:
- arXiv:1309.5593
- Bibcode:
- 2013JAP...113t3701Z
- Keywords:
-
- antiferromagnetic materials;
- calcium compounds;
- compressive strength;
- crystal defects;
- ferromagnetic materials;
- ferromagnetic-antiferromagnetic transitions;
- ferromagnetic-paramagnetic transitions;
- high-pressure effects;
- lanthanum compounds;
- lattice constants;
- magnetic anisotropy;
- magnetic epitaxial layers;
- neodymium compounds;
- paramagnetic materials;
- phase separation;
- 68.55.A-;
- 68.60.-p;
- 75.30.Gw;
- 75.30.Kz;
- 75.50.Ee;
- 75.70.Ak;
- 62.50.-p;
- Nucleation and growth;
- Physical properties of thin films nonelectronic;
- Magnetic anisotropy;
- Magnetic phase boundaries;
- Antiferromagnetics;
- Magnetic properties of monolayers and thin films;
- High-pressure effects in solids and liquids;
- Condensed Matter - Strongly Correlated Electrons;
- Condensed Matter - Materials Science
- E-Print:
- 17 pages,5 figures