Raman spectroscopy study of the interface structure in (CaCuO2)n/(SrTiO3)m superlattices
Abstract
Raman spectra of CaCuO2/SrTiO3 superlattices show clear spectroscopic marker of two structures formed in CaCuO2 at the interface with SrTiO3. For non-superconducting superlattices, grown in low oxidizing atmosphere, the 425 cm-1 frequency of oxygen vibration in CuO2 planes is the same as for CCO films with infinite layer structure (planar Cu-O coordination). For superconducting superlattices grown in highly oxidizing atmosphere, a 60 cm-1 frequency shift to lower energy occurs. This is ascribed to a change from planar to pyramidal Cu-O coordination because of oxygen incorporation at the interface. Raman spectroscopy proves to be a powerful tool for interface structure investigation.
- Publication:
-
Applied Physics Letters
- Pub Date:
- November 2013
- DOI:
- 10.1063/1.4828358
- arXiv:
- arXiv:1308.5616
- Bibcode:
- 2013ApPhL.103s1903D
- Keywords:
-
- calcium compounds;
- high-temperature superconductors;
- interface structure;
- oxidation;
- pulsed laser deposition;
- Raman spectra;
- spectrochemical analysis;
- strontium compounds;
- superconducting superlattices;
- superconducting thin films;
- vibrational modes;
- 74.25.Gz;
- 68.35.Ct;
- 74.72.Cj;
- 74.78.Fk;
- 78.30.Hv;
- 81.15.Fg;
- Optical properties;
- Interface structure and roughness;
- Multilayers superlattices heterostructures;
- Other nonmetallic inorganics;
- Laser deposition;
- Condensed Matter - Superconductivity;
- Condensed Matter - Materials Science
- E-Print:
- Appl. Phys. Lett. 103, 191903 (2013)