Thermal Conductivity and Annealing Effects in the Iron-Based Superconductor FeSe0.3Te0.7

Thermal conductivity measurements in magnetic fields have been performed for FeSe_0.3Te_0.7 single crystals as-grown and annealed at 400 °C for 100 h in vacuum (∼10^-4 Pa). It has been found that the thermal conductivity in the ab-plane, κ_ab, of the annealed crystal shows an enhancement at low temperatures just below the superconducting transition temperature, T_c, owing to the thermal conductivity due to quasiparticles, while the κ_ab of the as-grown crystal does not. This suggests that FeSe_1-xTe_x is a strongly correlated electron system. It has also been found that both the degree of the enhancement of κ_ab just below T_c and the behavior of the suppression of κ_ab by the application of magnetic field for the annealed crystal depend on the thickness of the crystal. These results indicate that bulk superconductivity is absent in the as-grown crystal, appears only in the surface area in the annealed-thick crystal and appears not only in the surface area but also inside of the annealed-thin crystal. It has been concluded that excess Fe included in the as-grown crystal is removed from the surface by annealing.