Enhancement in transport critical current density of ex situ PIT Ag/(Ba, K)Fe2As2 tapes achieved by applying a combined process of flat rolling and uniaxial pressing
Abstract
We report that the transport critical current density Jc of ex situ powder-in-tube (PIT) processed (Ba, K)Fe2As2 (Ba-122) tapes can be significantly enhanced by applying uniaxial cold pressing at the final stage of deformation. The tapes were prepared by packing high quality precursor powder into a Ag tube, cycles of rolling and intermediate annealing, and pressing followed by the final heat treatment for sintering. The Jc values in applied magnetic fields were increased by almost one order of magnitude compared to the tapes processed without pressing, exceeding 104 A cm-2 at 4.2 K. We achieved the highest Jc (at 4.2 K and 10 T) of 2.1×104 A cm-2 among PIT-processed Fe-based wires and tapes reported so far. The Jc-H curves measured at higher temperatures maintain small field dependence up to around 20 K, suggesting that these tapes are promising for applications at higher temperatures as well as at liquid helium temperature. The microstructure investigations reveal that there are two possible causes of the large Jc enhancement by pressing: one is densification and the other is the change of crack structure. Optimization of processing parameters such as the reduction ratio of rolling and pressing is expected to yield further Jc enhancement.
- Publication:
-
Superconductor Science Technology
- Pub Date:
- November 2013
- DOI:
- 10.1088/0953-2048/26/11/115007
- arXiv:
- arXiv:1304.3161
- Bibcode:
- 2013SuScT..26k5007T
- Keywords:
-
- Condensed Matter - Superconductivity
- E-Print:
- doi:10.1088/0953-2048/26/11/115007