Chromium-doped silica optical fibres: influence of the core composition on the Cr oxidation states and crystal field
Abstract
We have made chromium-doped, silica-based preforms and optical fibres by modified chemical vapour deposition (MCVD) and have studied the influence of the chemical composition of the doped region on the Cr-oxidation states and the spectroscopic properties of the samples. Chromium, introduced initially as Cr 3+, is partially or totally oxidized during the fabrication process, and is stabilized in the core of the preforms and fibres as Cr 3+ in octahedral coordination, and/or as Cr 4+ in distorded tetrahedral coordination (C s). Small concentrations (∼1-2 mol%) of codopants in silica, such as germanium or aluminium, suffice to promote a particular oxidation state. Particularly, 1 mol% of aluminium stabilizes all the present chromium into Cr 4+. The ligand field parameters, Dq, B and Dq/ B, for Cr 3+ and Cr 4+ are derived. It is shown that the chromium ions in our samples are in low-to-intermediate ligand field and that Dq and Dq/ B decrease when the aluminium content increases. The absorption cross-sections of Cr 3+ are similar to those reported in glasses and crystals, whereas Cr 4+ has lower values than the reference laser materials.
- Publication:
-
Optical Materials
- Pub Date:
- February 2001
- DOI:
- 10.1016/S0925-3467(00)00087-2
- arXiv:
- arXiv:1303.3835
- Bibcode:
- 2001OptMa..16..269F
- Keywords:
-
- Physics - Optics
- E-Print:
- Optical Materials 16 (2001) 269-277