Simultaneous measurement of pressure evolution of crystal structure and superconductivity in FeSe0.92 using designer diamonds
Abstract
Simultaneous high-pressure X-ray diffraction and electrical resistance measurements have been carried out on a PbO-type α-FeSe0.92 compound to a pressure of 44 GPa and temperatures down to 4 K using designer diamond anvils at synchrotron source. At ambient temperature, a structural phase transition from a tetragonal (P4/nmm) phase to an orthorhombic (Pbnm) phase is observed at 11 GPa and the Pbnm phase persists up to 74 GPa. The superconducting transition temperature (TC) increases rapidly with pressure reaching a maximum of ∼28 K at ∼6 GPa and decreases at higher pressures, disappearing completely at 14.6 GPa. Simultaneous pressure-dependent X-ray diffraction and resistance measurements at low temperatures show superconductivity only in a low-pressure orthorhombic (Cmma) phase of the α-FeSe0.92. Upon increasing pressure at 10 K near TC, crystalline phases change from a mixture of orthorhombic (Cmma) and hexagonal (P63/mmc) phases to a high-pressure orthorhombic (Pbnm) phase near 6.4 GPa where TC is maximum.
- Publication:
-
EPL (Europhysics Letters)
- Pub Date:
- July 2012
- DOI:
- 10.1209/0295-5075/99/26002
- arXiv:
- arXiv:1210.3645
- Bibcode:
- 2012EL.....9926002U
- Keywords:
-
- Condensed Matter - Superconductivity;
- Condensed Matter - Materials Science
- E-Print:
- 6 figures, 6 pages, Subjects: Superconductivity and Condensed matter (structural, mechanical &