Ferromagnetic ordering in CeIr2B2: Transport, magnetization, specific heat, and NMR studies

We present a complete characterization of the ferromagnetic system CeIr₂B₂ using powder x-ray diffraction (XRD), magnetic susceptibility χ(T), isothermal magnetization M(H), specific heat C(T), electrical resistivity ρ(T,H), and thermoelectric power S(T) measurements. Furthermore, ¹¹B NMR study was performed to probe the magnetism on a microscopic scale. Rietveld refinement of powder XRD data confirms that CeIr₂B₂ crystallizes in CaRh₂B₂-type orthorhombic structure (space group fddd). The χ(T), C(T), and ρ(T) data confirm bulk ferromagnetic ordering with T_c=5.1 K. Ce ions in CeIr₂B₂ are in a stable trivalent state. Our low-temperature C(T) data measured down to 0.4 K yield a Sommerfeld coefficient γ = 73(4) mJ/mol K², which is much smaller than the previously reported value of γ = 180 mJ/mol K² deduced from the specific heat measurement down to 2.5 K. For LaIr₂B₂, γ = 6(1) mJ/mol K², which implies the density of states at the Fermi level D(E_F)=2.54 states/(eV f.u.) for both spin directions. The renormalization factor for quasiparticle density of states and hence for quasiparticle mass due to 4f correlations in CeIr₂B₂ is ≈12. The Kondo temperature T_K∼4 K is estimated from the jump in specific heat of CeIr₂B₂ at T_c. Both C(T) and ρ(T) data exhibit a gapped-magnon behavior in the magnetically ordered state with an energy gap E_g∼3.5 K. The ρ data as a function of magnetic field H indicate a large negative magnetoresistance (MR) which is highest for T=5 K. While at 5 K the negative MR keeps on increasing up to 10 T, at 2 K an upturn is observed near H=3.5 T. On the other hand, the thermoelectric power data have small absolute values (S∼7μV/K), indicating a weak Kondo interaction. A shoulder in S(T) at about 30 K, followed by a minimum at ∼10 K, is attributed to crystal electric field effects and the onset of magnetic ordering. ¹¹B NMR line broadening provides strong evidence of ferromagnetic correlations below 40 K.