Finite-size effects in amorphous Fe90Zr10/Al75Zr25 multilayers

The thickness dependence of the magnetic properties of amorphous Fe₉₀Zr₁₀ layers is explored using Fe₉₀Zr₁₀/Al₇₅Zr₂₅ multilayers. The Al₇₅Zr₂₅ layer thickness is kept at 40 Å, while the thickness of the Fe₉₀Zr₁₀ layers is varied between 5 and 20 Å. The thickness of the Al₇₅Zr₂₅ layers is sufficiently large to suppress any significant interlayer coupling. Both the Curie temperature and the spontaneous magnetization decrease nonlinearly with decreasing thickness of the Fe₉₀Zr₁₀ layers. No ferromagnetic order is observed in the multilayer with 5-Å Fe₉₀Zr₁₀ layers. The variation of the Curie temperature T_c with the Fe₉₀Zr₁₀ layer thickness t is fitted with a finite-size scaling formula [1-T_c(t)/T_c(∞)]=[(t-t^')/t₀]^-λ, yielding λ=1.2, and a critical thickness t^'=6.5 Å, below which the Curie temperature is 0.