An experimental and theoretical study of the effect of temperature on the mechanical behavior of nanoclay reinforced polymers
Abstract
The goals of this study are to investigate the tensile loading and low velocity impact response of nanoclay reinforced polymers at various temperatures. Three types of polypropylene (PP 3371, Borealis and TP 3868) and epoxy with various nanoclay reinforcement percentages were considered. Tensile tests were conducted on ASTM Type I specimens instrumented with strain gauges using an MTS testing machine equipped with an environmental chamber. Low velocity impact tests were also performed using an Instron-Dynatup 8250 impact test machine equipped with an environmental chamber. Tensile test results were used to determine the effect of nanoclay reinforcement and different resins on the mechanical properties at various temperatures. The tensile tests results indicate that the Young's modulus of the nanocomposite increases with increasing nanoclay reinforcement percentage. The temperature has even a more significant effect. It was observed that as the temperature decreases the material becomes brittle, has higher stiffness and fails at lower strains. High temperatures have the opposite effect, in that, as the temperature increases the material loses stiffness and becomes more ductile. Temperature and nanoclay reinforcement affect the Poisson's ratio also, but this effect is less significant. In general, as the temperature increases the Poisson's ratio also increases. However, an increase in nanoclay reinforcement generally reduces the Poisson's ratio. The mechanical properties of polymer/clay nanocomposites were also calculated using the Mori-Tanaka formulation and the finite element method. Furthermore, the Mori-Tanaka model was modified to include the effect of temperature and voids. In the Mori-Tanaka formulation three types of nanoclay particle distribution was assumed: oriented nanoclay particles parallel to the direction of tensile loading, 2-D randomly distributed particles and 3-D randomly distributed particles. The finite element calculations were performed on a representative volume element having the same reinforcement percentage as the test specimens, with the nanoclay particles placed in a plane parallel to the loading direction. The comparison of theoretical and experimental results shows that both the Mori-Tanaka formulation and the finite element method provide effective tools to predict the mechanical properties of nanoclay reinforced composites. Furthermore, including the effect of temperature and voids provided a better match with experimental results.
- Publication:
-
Ph.D. Thesis
- Pub Date:
- 2012
- DOI:
- 10.48550/arXiv.1202.2960
- arXiv:
- arXiv:1202.2960
- Bibcode:
- 2012PhDT........20B
- Keywords:
-
- Chemistry, Polymer;Engineering, Mechanical;Engineering, Materials Science;
- Mathematics - Classical Analysis and ODEs;
- Mathematics - Optimization and Control;
- 26A33;
- 26E70;
- 39A12;
- 49K05
- E-Print:
- PhD thesis, Doctoral Programme in Mathematics and Applications (PDMA), University of Aveiro and University of Minho, 2012. Supervisor: Delfim F. M. Torres. Defended and approved 13/Feb/2012