Antiferromagnetic order and domains in Sr3Ir2O7 probed by x-ray resonant scattering

We report on a detailed x-ray resonant scattering study of the bilayer iridate compound Sr₃Ir₂O₇ at the Ir L₂ and L₃ edges. Resonant scattering at the Ir L₃ edge has been used to determine that Sr₃Ir₂O₇ is a long-range ordered antiferromagnet below T_N≈230K with an ordering wave vector q=((1)/(2),(1)/(2),0). The energy resonance at the L₃ edge was found to be a factor of ∼30 times larger than that at the L₂ edge. This remarkable effect has been seen in the single-layer compound Sr₂IrO₄ and has been linked to the observation of a J_eff=(1)/(2) spin-orbit insulator. Our result shows that despite the modified electronic structure of the bilayer compound, caused by the larger bandwidth, the effect of strong spin-orbit coupling on the resonant magnetic scattering persists. Using the program sarah, we have determined that the magnetic order consists of two domains with propagation vectors k₁=((1)/(2),(1)/(2),0) and k₂=((1)/(2),-(1)/(2),0), respectively. A raster measurement of a focused x-ray beam across the surface of the sample yielded images of domains of the order of 100μm, with odd and even L components, respectively. Fully relativistic, monoelectronic calculations using the Green's function technique for a muffin-tin potential have been employed to calculate the relative intensities of the L_2,3 edge resonances, comparing the effects of including spin-orbit coupling and the Hubbard U term. A large L₃ to L₂ edge intensity ratio (∼5) was found for calculations including spin-orbit coupling. Adding the Hubbard U term had no significant effect on the calculated spectra.