Doping-dependent superconducting gap anisotropy in the two-dimensional pnictide Ca10(Pt3As8)[(Fe1-xPtx)2As2]5
Abstract
The characteristic features of the Ca10(Pt3As8)[(Fe1-xPtx)2As2]5 (the “10-3-8” phase) superconductor are triclinic symmetry, high anisotropy, and a clear separation of superconducting and antiferromagnetic regions in the T versus doping (x) phase diagram, which enables the superconducting gap to be studied without complications due to the coexisting magnetic order. The London penetration depth, measured on the underdoped side of the superconducting “dome” (x= 0.028, 0.041, 0.042, and 0.097), shows behavior remarkably similar to other Fe-based superconductors, exhibiting a robust power law, Δλ(T)=ATn. The exponent n decreases from 2.36 (x= 0.097, close to the optimal doping) to 1.7 (x= 0.028, a heavily underdoped composition), suggesting that the superconducting gap becomes more anisotropic at the dome edge. A similar trend is found in the lower anisotropy BaFe2As2 (“122”) -based superconductors, implying that it is an intrinsic property, unrelated to the coexistence of magnetic order and superconductivity or the anisotropy of the normal state.
- Publication:
-
Physical Review B
- Pub Date:
- January 2012
- DOI:
- 10.1103/PhysRevB.85.020504
- arXiv:
- arXiv:1111.1003
- Bibcode:
- 2012PhRvB..85b0504C
- Keywords:
-
- 74.70.Xa;
- 74.20.Rp;
- 74.62.En;
- Pairing symmetries;
- Condensed Matter - Superconductivity
- E-Print:
- Phys. Rev. B 85, 020504(R) (2012)