Temperature dependence of core loss in cobalt substituted Ni-Zn-Cu ferrites
Abstract
The temperature dependence of core loss in cobalt substituted Ni-Zn-Cu ferrites was investigated. Co2+ ions are known to lead to a compensation of the magneto-crystalline anisotropy in Ni-Zn ferrites, at a temperature depending on the cobalt content and the Ni/Zn ratio. We observed similar behaviour in Ni-Zn-Cu and it was found that the core loss goes through a minimum around this magneto-crystalline anisotropy compensation. Moreover, the anisotropy induced by the cobalt allowed a strong decrease of core loss, a ferrite having a core loss of 350 mW/cm3 at 80 °C was then developed (measured at 1.5 MHz and 25 mT). This result represents an improvement of a factor 4 compared to the state of art Ni-Zn ferrites.
- Publication:
-
Journal of Magnetism and Magnetic Materials
- Pub Date:
- March 2011
- DOI:
- 10.1016/j.jmmm.2010.10.037
- arXiv:
- arXiv:1103.5021
- Bibcode:
- 2011JMMM..323..735L
- Keywords:
-
- Condensed Matter - Materials Science
- E-Print:
- Journal of Magnetism and Magnetic Materials 323, 6 (2010) 735-739