Low-temperature synthesis of FeTe0.5Se0.5 polycrystals with a high transport critical current density
Abstract
We have prepared high-quality polycrystalline FeTe0.5Se0.5 at temperature as low as 550 °C. The transport critical current density evaluated from the current-voltage characteristics is over 700 A cm - 2 at 4.2 K under zero field, which is several times larger than that for FeTe0.5Se0.5 superconducting wires. The critical current density estimated from magneto-optical images of flux penetration is also similar to this value. The upper critical field of the polycrystalline FeTe0.5Se0.5 at T = 0 K estimated using Werthamer-Helfand-Hohenberg theory is 585 kOe, which is comparable to that of single crystals. This study gives some insight into how to improve the performance of FeTe0.5Se0.5 superconducting wires.
- Publication:
-
Superconductor Science Technology
- Pub Date:
- July 2011
- DOI:
- 10.1088/0953-2048/24/7/075025
- arXiv:
- arXiv:1103.1809
- Bibcode:
- 2011SuScT..24g5025D
- Keywords:
-
- Condensed Matter - Superconductivity
- E-Print:
- 12 pages, 6 figures