Large Transport Critical Current Densities of Ag Sheathed (Ba,K)Fe2As2+Ag Superconducting Wires Fabricated by an Ex-situ Powder-in-Tube Process
Abstract
We report large transport critical current densities observed in Ag-added (Ba,K)Fe2As2 superconducting wires prepared by an ex-situ powder-in-tube (PIT) process. The wire has a simple composite structure sheathed only by Ag. A precursor bulk material prepared by a melting process was ground into powder and put into a Ag tube. The composite was then cold worked into a wire and heat treated at 850 °C for sintering. Transport critical current densities, Jc, at 4.2 K are 1.0×104 A/cm2 (Ic = 60.7 A) in self field and 1.1×103 A/cm2 (Ic = 6.6 A) in 10 T. These are the highest values reported so far for the Fe-based superconducting wires.
- Publication:
-
Applied Physics Express
- Pub Date:
- April 2011
- DOI:
- 10.1143/APEX.4.043101
- arXiv:
- arXiv:1103.1701
- Bibcode:
- 2011APExp...4d3101T
- Keywords:
-
- Condensed Matter - Superconductivity
- E-Print:
- in press for Appl. Phys. Express