Se77 NMR investigation of the KxFe2-ySe2 high-Tc superconductor (Tc=33 K)

We report comprehensive Se77 NMR measurements on a single crystalline sample of the recently discovered FeSe-based high-temperature superconductor K_xFe_2-ySe₂ (T_c=33 K) in a broad temperature range up to 290 K. Despite deviations from the stoichiometric KFe₂Se₂ composition, we observed Se77 NMR line shapes as narrow as 4.5 kHz under a magnetic field applied along the crystal c axis, and found no evidence for co-existence of magnetic order with superconductivity. On the other hand, the Se77 NMR line shape splits into two peaks with equal intensities at all temperatures when we apply the magnetic field along the ab plane. This suggests that K vacancies may have a superstructure and that the local symmetry of the Se sites is lower than the tetragonal fourfold symmetry of the average structure. This effect might be a prerequisite for stabilizing the s_± symmetry of superconductivity in the absence of the hole bands at the Brillouin zone center. From the increase of NMR linewidth below T_c induced by the Abrikosov lattice of superconducting vortices, we estimate the in-plane penetration depth λ_ab~290 nm and the carrier concentration n_e~1×10⁺²¹ cm^-3. Our Knight shift ⁷⁷K data indicate that the uniform spin susceptibility decreases progressively with temperature, in analogy with the case of FeSe (T_c~9 K) as well as other FeAs high-T_c systems. The strong suppression of ⁷⁷K observed immediately below T_c for all crystal orientations is consistent with a singlet pairing of Cooper pairs. We do not however observe the Hebel-Slichter coherence peak of the nuclear spin-lattice relaxation rate 1/T₁ immediately below T_c, expected for conventional BCS s-wave superconductors. In contrast with the case of FeSe, we do not observe evidence for an enhancement of low-frequency antiferromagnetic spin fluctuations near T_c in 1/T₁T. Instead, 1/T₁T exhibits qualitatively the same behavior as overdoped non-superconducting Ba(Fe_1-xCo_x)₂As₂ with x~0.14 or greater, where hole bands are missing in the Brillouin zone center. We will discuss the implications of our results on the unknown mechanism of high-temperature superconductivity in FeSe and FeAs systems.