Possible coexistence of superconductivity and magnetism in intermetallic NiBi 3
Abstract
NiBi3 polycrystals were synthesized via a solid state method. X-ray diffraction analysis shows that the main phase present in the sample corresponds to NiBi3 in a weight fraction of 96.82 % according to the refinement of the crystalline structure. SEM - EDS and XPS analysis reveal a homogeneous composition of NiBi3, without Ni traces. The powder superconducting samples were studied by performing magnetic measurements. The superconducting transition temperature and critical magnetic fields were determined as TC=4.05 K, HC1=110 Oe and HC2=3,620 Oe. The superconducting parameters were ξGL=301.5 Å, λGL=1549 Å, and κ=5.136. Isothermal measurements below the transition temperature show an anomalous behavior. Above the superconducting transition the compound presents ferromagnetic characteristics up to 750 K, well above the Ni Curie temperature.
- Publication:
-
Solid State Communications
- Pub Date:
- March 2011
- DOI:
- 10.1016/j.ssc.2011.01.005
- arXiv:
- arXiv:1101.2226
- Bibcode:
- 2011SSCom.151..425P
- Keywords:
-
- Condensed Matter - Superconductivity
- E-Print:
- Accepted in Solid State Communications