High-temperature magnetic properties of noninteracting randomly oriented single-domain Fe 3 - δO 4 nanoparticles

Magnetic measurements have been performed on 40-nm sphere-like Fe _{3 - δ}O ₄ ( δ=0.043) nanoparticles using a Quantum Design vibrating sample magnetometer. Coating Fe _{3 - δ}O ₄ nanoparticles with SiO ₂ effectively eliminates magnetic interparticle interactions so that the coercive field H in the high-temperature range between 300 K and the Curie temperature (855 K) can be well fitted by an expression for noninteracting randomly oriented single-domain particles. From the fitting parameters, the effective anisotropy constant K is found to be (1.38±0.11)×10 erg/cm, which is very close to the bulk magnetocrystalline anisotropy constant of 1.35×10 erg/cm. Moreover, the inferred mean particle diameter from the fitting parameters is in quantitative agreement with that determined from transmission electron microscope. Such a quantitative agreement between data and theory suggests that the ensemble of our SiO ₂-coated sphere-like Fe _{3 - δ}O ₄ nanoparticles represents a good system of noninteracting randomly-oriented single-domain particles.