Magnetic properties of σ-FeCr alloys as calculated with the charge- and spin-self-consistent KKR(CPA) method

Magnetic properties of a σ-Fe₁₆Cr₁₄ alloy calculated with the charge- and spin-self-consistent Korringa-Kohn-Rostoker (KKR) and combined with coherent potential approximation (KKR-CPA) methods are reported. Nonmagnetic state as well as various magnetic orderings were considered, i.e., ferromagnetic (FM) and more complex antiparallel (called APM) arrangements for selected sublattices, as follows from the symmetry analysis. It has been shown that the Stoner criterion applied to nonmagnetic density of states at the Fermi energy, E_F is satisfied for Fe atoms situated on all five lattice sites, while it is not fulfilled for all Cr atoms. In FM and APM states, the values of magnetic moments on Fe atoms occupying various sites are dispersed between 0 and 2.5μ_B , and they are proportional to the number of Fe atoms in the nearest-neighbor shell. Magnetic moments of Cr atoms having much smaller values were found to be coupled antiparallel to those of Fe atoms. The average value of the magnetic moment per atom was found to be ⟨μ⟩=0.55μ_B that is by a factor of 4 larger than the experimental value found for a σ-Fe_0.538Cr_0.462 sample. Conversely, admitting an antiparallel ordering (APM model) on atoms situated on C and D sites, according to the group theory and symmetry analysis results, yielded a substantial reduction of ⟨μ⟩ to 0.20μ_B . Further diminution of ⟨μ⟩ to 0.15μ_B , which is very close to the experimental value of 0.14μ_B , has been achieved with the KKR-CPA calculations by considering a chemical disorder on sites B, C, and D.