Pseudogap and its critical point in the heavily doped Ba(Fe1-xCox)2As2 from c -axis resistivity measurements

Temperature-dependent interplane resistivity, ρ_c(T) , was used to characterize the normal state of the iron-arsenide superconductor Ba(Fe_1-xCo_x)₂As₂ over a broad doping range 0≤x<0.50 . The data were compared with in-plane resistivity, ρ_a(T) , and magnetic susceptibility, χ(T) , taken in H⊥c , as well as Co NMR Knight shift, K59 , and spin-relaxation rate, 1/T₁T . The interplane resistivity data show a clear correlation with the NMR Knight shift, assigned to the formation of the pseudogap. Evolution of ρ_c(T) with doping reveals two characteristic energy scales. The temperature of the crossover from nonmetallic, increasing on cooling, behavior of ρ_c(T) at high temperatures to metallic behavior at low temperatures, T^∗ , correlates well with an anomaly in all three magnetic measurements. This characteristic temperature, equal to approximately 200 K in the parent compound, x=0 , decreases with doping and vanishes near x^∗≈0.25 . For doping levels x≥0.166 , an additional feature appears above T^∗ with metallic behavior of ρ_c(T) found above the low-temperature resistivity increase. The characteristic temperature of this charge-gap formation, T_CG , vanishes at x_CG≃0.30 , paving the way to metallic, T linear, ρ_c(T) close to x_CG and superlinear T dependence for x>x_CG . None of these features are evident in the in-plane resistivity ρ_a(T) . For doping levels x<x_CG , χ(T) shows a known, anomalous, T -linear dependence, which disappears for x>x_CG . These features are consistent with the existence of a charge gap, accompanying formation of the magnetic pseudogap, and its critical suppression with doping. The inferred c -axis charge gap reflects the three-dimensional character of the electronic structure and of the magnetism in the iron arsenides.