Synthesis, anisotropy, and superconducting properties of LiFeAs single crystal
Abstract
A LiFeAs single crystal with Tconset∼19.7 K was grown in a sealed tungsten crucible using the Bridgeman method. The electrical resistivity experiments revealed a ratio of room temperature to residual resistivity of approximately 46 and 18 for the in-plane and out-of plane directions, respectively. The estimated anisotropic resistivity, γρ=ρc/ρab, was approximately 3.3 at Tconset. The upper critical fields had large Hc2∥ab and Hc2∥c values of 83.4 T and 72.5 T, respectively, and an anisotropy ratio is γH=Hc2∥ab/Hc2∥c∼1.15. The high upper critical field value and small anisotropy highlight the potential use of LiFeAs in a variety of applications. The calculated critical current density (Jc) from the M-H loop is approximately 103 A/cm2
- Publication:
-
Applied Physics Letters
- Pub Date:
- May 2010
- DOI:
- 10.1063/1.3435472
- arXiv:
- arXiv:1002.2249
- Bibcode:
- 2010ApPhL..96u2508S
- Keywords:
-
- critical current density (superconductivity);
- crystal growth from melt;
- electrical resistivity;
- high-temperature superconductors;
- lithium compounds;
- superconducting critical field;
- 81.10.Fq;
- 74.25.Op;
- 74.25.Sv;
- 74.81.-g;
- Growth from melts;
- zone melting and refining;
- Mixed states critical fields and surface sheaths;
- Critical currents;
- Inhomogeneous superconductors and superconducting systems;
- Condensed Matter - Superconductivity;
- Condensed Matter - Materials Science
- E-Print:
- 4 pages, 4 figures