Flux growth at ambient pressure of millimeter-sized single crystals of LaFeAsO, LaFeAsO1-xFx, and LaFe1-xCoxAsO
Abstract
Millimeter-sized single crystals of LaFeAsO, LaFeAsO1-xFx, and LaFe1-xCoxAsO were grown in NaAs flux at ambient pressure. The detailed growth procedure and crystal characterizations are reported. The as-grown crystals have typical dimensions of 3×4×0.05-0.3 mm3 with the crystallographic c-axis perpendicular to the plane of the platelike single crystals. Various characterizations confirmed the high quality of our LaFeAsO crystals. Co and F were introduced into the lattice leading to superconducting LaFe1-xCoxAsO and LaFeAsO1-xFx single crystals, respectively. This growth protocol is expected to be broadly applicable to grow other RMAsO (R =rare earth, M =transition metal) compounds.
- Publication:
-
Applied Physics Letters
- Pub Date:
- November 2009
- DOI:
- 10.1063/1.3268435
- arXiv:
- arXiv:0909.3510
- Bibcode:
- 2009ApPhL..95v2504Y
- Keywords:
-
- cobalt compounds;
- crystal growth from solution;
- electrical resistivity;
- high-temperature superconductors;
- iron compounds;
- lanthanum compounds;
- lattice constants;
- magnetic susceptibility;
- magnetisation;
- 81.10.Dn;
- 74.72.-h;
- 61.66.Fn;
- 74.25.Ha;
- Growth from solutions;
- Cuprate superconductors;
- Inorganic compounds;
- Magnetic properties;
- Condensed Matter - Superconductivity;
- Condensed Matter - Strongly Correlated Electrons
- E-Print:
- Applied Physics Letters, 95, 222504 (2009)