Mn valence instability in La2/3 Ca1/3 Mn O3 thin films

A Mn valence instability on La_2/3Ca_1/3MnO₃ thin films, grown on LaAlO₃ (001) substrates is observed by x-ray absorption spectroscopy at the Mn L -edge and O K -edge. As-grown samples, in situ annealed at 800°C in oxygen, exhibit a Curie temperature well below that of the bulk material. Upon air exposure a reduction of the saturation magnetization, M_S , of the films is detected. Simultaneously a Mn²⁺ spectral signature develops, in addition to the expected Mn³⁺ and Mn⁴⁺ contributions, which increases with time. The similarity of the spectral results obtained by total electron yield and fluorescence yield spectroscopy indicates that the location of the Mn valence anomalies is not confined to a narrow surface region of the film, but can extend throughout the whole thickness of the sample. High temperature annealing at 1000°C in air, immediately after growth, improves the magnetic and transport properties of such films towards the bulk values and the Mn²⁺ signature in the spectra does not appear. The Mn valence is then stable even to prolonged air exposure. We propose a mechanism for the Mn²⁺ ions formation and discuss the importance of these observations with respect to previous findings and production of thin films devices.