Raman scattering from the CaC6 superconductor in the presence of disorder

Polarized Raman scattering has been performed on CaC₆ superconductor. We identify two of the three Raman-active E_g phonon modes at 440 and 1508cm^-1 expected for the R3¯m space group of CaC₆ . These first-order scattering modes appear along with the D and G bands around 1300 and 1600cm^-1 that are similar in origin to the corresponding bands in plain graphite. The intensities of the D and G bands in CaC₆ correlate with degree of disorder. The D band arises from the double resonant Raman-scattering process; its frequency shifts as a function of excitation energy with ∼35cm^-1/eV . The double resonant Raman scattering probes phonon excitations with finite wave vector q . We estimate the characteristic spacing of structural defects to be on the scale of about 100Å by comparing the intensity of the D band and the 1508cm^-1 E_g mode in CaC₆ to calibrated intensity ratio of analogous bands in disordered graphites. A sharp superconducting coherence peak at 24cm^-1 is observed below T_c .