Synthesis and magnetic characterization of TmCo2B2C

A new quaternary intermetallic borocarbide TmCo₂B₂C has been synthesized via rapid-quench of an arc-melted ingot. Elemental and powder-diffraction analyses established its correct stoichiometry and single-phase character. The crystal structure is isomorphous with that of TmNi₂B₂C (I4/mmm) and is stable over the studied temperature range. Above 7 K, the paramagnetic state follows modified Curie-Weiss behavior (χ = C/(T-θ)+χ₀) wherein χ₀ = 0.008(1) emu mol^-1 with the temperature-dependent term reflecting the paramagnetism of the Tm subsystem: μ_eff = 7.6(2) μ_B (in agreement with the expected value for a free Tm³⁺ ion) and θ = -4.5(3) K. Long-range ferromagnetic order of the Tm sublattice is observed to develop around ~1 K. No superconductivity is detected in TmCo₂B₂C down to 20 mK, a feature which is consistent with the general trend in the RCo₂B₂C series. Finally, the influence of the rapid-quench process on the magnetism (and superconductivity) of TmNi₂B₂C will be discussed and compared to that of TmCo₂B₂C.