Abstract
We report the synthesis, magnetic susceptibility and crystal structure analysis for NbB (x=0.0-1.0) samples. The study helps find a correlation among the lattice parameters, chemical composition and the superconducting transition temperature Tc. Rietveld analysis is done on the X-ray diffraction patterns of all synthesized samples to determine the lattice parameters. The a parameter decreases slightly and has a random variation with increasing x, while c parameter increases from 3.26 for pure NbB 2 to 3.32 for x=0.4 i.e. NbB 2.4. With higher Boron content (x>0.4) the c parameter decreases slightly. The stretching of lattice in c direction induces superconductivity in the non-stoichiometric niobium boride. Pure NbB 2 is non-superconductor while the other NbB (x>0.0) samples show diamagnetic signal in the temperature range 8.9-11 K. Magnetization measurements ( M-H) at a fixed temperature of 5 K are also carried out in both increasing and decreasing directions of field. The estimated lower and upper critical fields ( H & H) as viewed from M-H plots are around 590 and 2000 Oe, respectively, for NbB 2.6 samples. In our case, superconductivity is achieved in NbB 2 by varying the Nb/B ratios, rather than changing the processing conditions as reported by others.
- Publication:
-
Solid State Communications
- Pub Date:
- September 2008
- DOI:
- 10.1016/j.ssc.2008.07.006
- arXiv:
- arXiv:0807.1198
- Bibcode:
- 2008SSCom.147..439M
- Keywords:
-
- Condensed Matter - Superconductivity;
- Condensed Matter - Strongly Correlated Electrons
- E-Print:
- 14 pages TEXT+Figs