Thermodynamic properties of Ba1-xKxFe2As2 and Ca1-xNaxFe2As2
Abstract
The specific heat C(T) of a BaFe2As2 single crystal and hole-doped superconducting Ba0.5K0.5Fe2As2 and Ca0.5Na0.5Fe2As2 polycrystals were measured. For the undoped BaFe2As2 single crystal, a very sharp specific heat peak was observed at 136 K. This is attributed to the structural and antiferromagnetic transitions occurring at the same temperature. For the superconducting Ba0.5K0.5Fe2As2 polycrystal, a clear peak of C/T was observed at Tc=36 K, which is the highest peak seen at a superconducting transition for iron-based high-Tc superconductors so far. For the superconducting Ca0.5Na0.5Fe2As2 sample with lower Tc=18 K, there is no obvious anomaly in C/T below Tc, which may be due to its low superfluid density. The electronic specific heat coefficients γ and Debye temperatures ΘD of these compounds were obtained from the low-temperature data.
- Publication:
-
New Journal of Physics
- Pub Date:
- December 2008
- DOI:
- 10.1088/1367-2630/10/12/123031
- arXiv:
- arXiv:0806.3573
- Bibcode:
- 2008NJPh...10l3031D
- Keywords:
-
- Condensed Matter - Superconductivity;
- Condensed Matter - Strongly Correlated Electrons
- E-Print:
- New Journal of Physics 10 (2008) 123031